Photoluminescence of transparent strontium-barium-niobate-doped silica nanocomposites

S. G. Lu, Chee Leung Mak, K. H. Wong, K. W. Cheah

Research output: Journal article publicationJournal articleAcademic researchpeer-review

12 Citations (Scopus)


Optically transparent nanocomposites of strontium-barium-niobate (SBN) and silica were fabricated via a novel sol-gel method. The nanocomposites were annealed in temperatures of 600-800 °C to yield the nanometer-sized tetragonal tungsten-bronze phase of SBN crystallites. Photoluminescence studies at temperatures from 10 K to room temperature were performed. The undoped silica matrix showed a strong emission band at 3.2 eV and a weak emission band at 2.65 eV. They were noticeably suppressed in our SBN/SiO2nanocomposites. Extra sharp peaks on top of the 3.2 eV band were seen. An additional emission band at 2.3 eV due to transitions within the NbO6complex of SBN crystallites was also observed. This emission band showed a large blueshift with decreasing SBN crystallite size. This demonstrates that the photoluminescence spectra of ferroelectric-doped silica nanocomposites have a strong dependence on crystallite size.
Original languageEnglish
Pages (from-to)4310-4312
Number of pages3
JournalApplied Physics Letters
Issue number26
Publication statusPublished - 24 Dec 2001

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)


Dive into the research topics of 'Photoluminescence of transparent strontium-barium-niobate-doped silica nanocomposites'. Together they form a unique fingerprint.

Cite this