Keyphrases
Elevated Temperature
100%
Mechanical Characterization
100%
Double Strap Joint
100%
Ultimate Load
66%
Effective Bond Length
66%
Adherend
33%
Bond Length
33%
Mechanical Performance
33%
Mechanistic Model
33%
Glass Transition Temperature
33%
Joint Stiffness
33%
Stiffness Degradation
33%
Strength Degradation
33%
Bond Strength
33%
Kinetic Model
33%
Debonding Failure
33%
Double-lap Joint
33%
Load Prediction Model
33%
Joint Modeling
33%
Mechanical Degradation
33%
Loading Stiffness
33%
Adhesively Bonded
33%
Bond Stiffness
33%
Joint Failure Mode
33%
Modeling Results
33%
Engineering
Elevated Temperature
100%
Joints (Structural Components)
100%
Double Strap Joint
100%
Mechanical Performance
33%
Experimental Measurement
33%
Stiffness Degradation
33%
Glass Transition Temperature (Tg)
33%
Double Lap Joint
33%
Strength Degradation
33%
Debonding
33%
Mechanical Degradation
33%
Failure Mode
33%
Material Science
Mechanical Testing
100%
Debonding
100%
Glass Transition Temperature
100%
Mechanical Degradation
100%