Fabrication and characterization of poly-d-l-lactide/nano-hydroxyapatite composite scaffolds with poly (ethylene glycol) coating and dexamethasone releasing

Keyphrases

• Polyethylene Glycol 100%
• Poly(D,L-lactide) 100%
• Nano-hydroxyapatite Composite 100%
• Composite Scaffold 100%
• Nano-HAP 100%
• Compression Molding 33%
• Coagulation 33%
• Coating Process 33%
• Pore Structure 33%
• Pore Size 33%
• Compressive Strength 33%
• High Porosity 33%
• Compressive Modulus 33%
• Biodegradation 33%
• Porosity Level 33%
• Bone Tissue Engineering 33%
• Nano-hydroxyapatite (n-HA) 33%
• Surface Hydrophobicity 33%
• Drug Loading 33%
• Particulate Leaching 33%
• Hydroxyapatite Scaffold 33%
• Loading Amount 33%
• Drug Coating 33%
• Drug Release 33%
• Pore Network 33%
• Release Capacity 33%
• Drug Release Behavior 33%
• Cold Compression 33%
• Controllable Pore Size 33%
• Immersion in Water 33%

Chemical Engineering

• Hydroxyapatite 100%
• Polyethylene Glycol 100%
• Biodegradation 33%
• Loading Amount 33%