Effect of reinforcing tabs on the mode I delamination toughness of stitched CFRPs

Keyphrases

• Toughness 100%
• Resin Transfer Molding 100%
• Delamination Toughness 100%
• Mode I Delamination 100%
• Resin 50%
• Steady State 50%
• Carbon Fiber Composite 50%
• Cantilever 50%
• Reinforced 50%
• Micromechanical Modeling 50%
• Molding Process 50%
• Failure Mechanism 50%
• Crack Propagating 50%
• Self-similarity 50%
• Prepreg 50%
• Composite Specimen 50%
• Stitch Density 50%
• Double Cantilever Beam Specimen 50%
• Carbon Cloth 50%
• Interlaminar Fracture Toughness 50%
• Double Cantilever Beam Test 50%
• Through-thickness Direction 50%
• Mode I Toughness 50%
• Mode I Testing 50%
• Prepreg Tape 50%
• Stitching Thread 50%
• Unidirectional Prepreg 50%

Engineering

• Delamination 100%
• Resin Transfer Molding 100%
• Experimental Result 50%
• Good Agreement 50%
• Carbon Fibre Composite 50%
• Beam Specimen 50%
• Thickness Direction 50%
• Composite Specimen 50%
• Propagating Crack 50%
• Double-Cantilever Beam 50%
• Double Cantilever Beam Test 50%
• Micromechanics 50%
• Failure Mechanism 50%
• Fracture Strength 50%

Material Science

• Composite Material 100%
• Resin Transfer Molding 100%
• Delamination 100%
• Prepreg 100%
• Fracture Toughness 50%
• Kevlar 50%
• Molding 50%
• Carbon Fiber 50%
• Aluminum 50%
• Density 50%
• Micromechanics 50%